Fluorine Chemical, Lithopone 30% CAS No. 1345-05-7, white powder, relative density: 4.136 ~ 4.39 g / mL, insoluble in water. It is a mixture of zinc sulfide and barium sulfate. Inorganic white pigment, widely used in plastics such as polyolefin, vinyl resin, ABS resin, polystyrene, polycarbonate, nylon and polyoxymethylene, and white pigments of paints and inks. It is less effective in polyurethane and amino resins and less suitable in fluoroplastics. It is also used for coloring of rubber products, paper, varnish, tarpaulin, leather, watercolor paint, paper, enamel, and the like. Used as a binder in the production of electric beads.

Algaecidal effect of Lithopon: After 5 years of exposure to weathering in Alpen (Lower Rhine)  

Although barium sulfate is almost completely inert, zinc sulfide degrades upon exposure to UV light, leading to darkening of the pigment. The severity of this UV reaction is dependent on a combination of two factors; how much zinc sulfide makes up the pigments formulation, and its total accumulated UV exposure. Depending on these factors Lithopone B301, Lithopone B311 powder itself may vary in shade over time, ranging from pure white all the way to grey or even black. To suppress this effect, a dopant might be used, like small amount of cobalt salts, which would be added to the formulation. This process creates cobalt-doped zinc sulfide. The cobalt salts help to stabilize zinc sulfide so it will not have as severe a reaction to UV exposure.

The produced barium sulfide enters the leacher, and the temperature is controlled above 65°C to obtain a barium sulfide content of 70%, and then enters the clarification barrel, add zinc sulfate for reaction after clarification, control the zinc sulfate content to be greater than 28%, pH=8~9, and obtain a mixture of barium sulfate and zinc sulfide with a density of 1.296~1.357 g/cm3.

The production of ROS was studied on white blood cells as a model to screen the effect on eukaryotic cells after being exposed to samples and solar simulated irradiation (according to the level of penetration under the skin). For that purpose, the leukocytes were separated from anticoagulated fresh blood using the Ficoll-Hypaque reactive in a well-known technique [33]. Then, 50 μL of suspensions of P25TiO₂NPs (0.2 mg/mL and 0.02 mg/mL), vitaminB2@P25TiO₂NPs (0.2 mg/mL and 0.02 mg/mL) and vitamin B2 (0.2 mg/mL and 0.02 mg/mL) were prepared and mixed with 50 μL of white blood cells suspension. A solution of 3% H₂O₂ was used as positive control and PBS as negative control. Then, the samples were irradiated using the LED panel for 3 and 6 h to simulate the light penetration into the skin. Also, a set of samples was kept in the dark as control. Finally, the ROS were detected through the colorimetric assay employing the nitroblue tetrazolium salt (NBT salt) and the absorbance at 650 nm was measured. The experiment was reproduced twice; the standard deviation was calculated and p-value < 0.05 were considered significant.

Food preservation and packaging

Titanium dioxide (TiO₂) is by far the most suited white pigment to obtain whiteness and hiding power in coatings, inks and plastics. This is because it has an extremely high refractive index and it does not absorb visible light. TiO₂ is also readily available as particles with the right size (d ≈ 280 nm) and the right shape (more or less spherical) as well as with a variety of post-treatments.

However, the pigment is expensive, especially when the volume prices of systems are used. And, there always remains a need to develop a full-proof strategy to obtain the best results in terms of cost/performance ratio, scattering efficiency, dispersion… while using it in coating formulations. Are you searching for the same?

Explore the detailed knowledge of TiO₂ pigment, its scattering efficiency, optimization, selection, etc. to achieve the best possible white color strength and hiding power in your formulations.

In terms of application, meticulous preparation and attention to detail yield the best results. For paint grinders, maintaining a ratio of 12 pounds of refined linseed oil to 88 pounds of lithopone pigment will provide optimal workability. A salient factor that should be heeded is the state of the lithopone before mixing with oil; the material must be sufficiently dry. Only then will it integrate seamlessly with the oil, ensuring that the resultant mixture possesses the desired consistency and properties.

0.3% Max

≥99.0