If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.

Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.

Steel mesh jinsu appearance treatment: polyethylene thermoplastic powder coatings is also called polyethylene powder coating, is the high pressure polyethylene (LDPE) as the basic material, adding a variety of function additives, colors, its antiseptic powder coating manufacturing processes, jinsu coating layer has the function of chemical, shock, circuitous, acid, salt fog corrosion, decorate a function and has good appearance.

Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements. Galvanized iron wire equipment is specially used for the plating of iron. Generally speaking, the stability of zinc is much higher than that of iron, and it will not rust in the daily water vapor or damp place.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

Large roll galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Large roll galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics.

Iron and steel in the condition of cooling on the surface galvanized, and hot dip galvanized steel pipe in the condition of hot dip on the surface, its adhesion is strong, not easy to fall off, hot dip galvanized pipe although also rust phenomenon, but in a long period can meet the technical and sanitary requirements.

Cold wire drawing is a kind of cold processing of metal, that is, we often say reinforcement. Cold drawing process is not messy, cold drawing price based on the quality of cold drawing dividends of different levels, cold drawing production is also a variety of different procedures. The main factor affecting the strength of cold drawing wire is raw materials, which are closely related to the raw materials, strength and diameter of raw materials, and the better the quality of cold drawing wire, the more messy the production process.